Cold Applied Bituminous Waterproofing Coating Polymer Modified Asphalt For Engineering Projects

Product Categories

Weifang Shihua Chemical Building Material Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Supply Ability : 1000000kg per Month

Low‑temperature Flexibility : No cracking at 0℃

Brand Name : shhous

Elongation at Break : ≥600%

Model Number : Liquid asphalt paste, one‑component

Application Method : Cold application, roller / brush / trowel applicable

MOQ : 1000kg

Color : Black

Price : USD 0.5‑0.8/kg

Solid Content : ≥45%

Packaging Details : Metal Barrel

Certification : ISO

Product Form : Liquid Coating

Place of Origin : Shandong, China

Film‑forming Substance : Polymer modified asphalt system

Contact Now

Cold Applied Polymer Modified Asphalt Waterproof Coating For Engineering Projects

Product Advantages

Excellent film elasticity: Polymer‑modified formula, cured film has good elongation to accommodate minor substrate cracking and deformation.
Superior waterproof sealing: Liquid applied, seamless continuous waterproof film to block capillary pores.
Good substrate adaptability: Applicable on damp substrates, strong adhesion to concrete, cement mortar and partial metal surfaces.
Easy detail treatment: Easy brushing on complex areas such as corners, pipe roots and construction joints for reinforcement.
Water & aging resistance: Polymer‑asphalt compound resists water immersion, acid and alkali, durable for underground and indoor conditions.
Safe cold‑applied work: Room‑temperature brushing, no open‑flame heating, simple operation without hot‑work risk.
Compatible with waterproof membranes: Good compatibility with asphalt self‑adhesive membranes for composite waterproofing system.

Performance Indexes

No.	Inspection Item		Technical Requirement
1	Appearance		After stirring, the sample shall be uniform without color difference, gel, agglomerate and obvious asphalt filaments
2	Solid content, %		≥45
3	Heat resistance		No flowing, slipping or dripping at 110 ℃
4	Surface drying time, h		≤8
5	Hard drying time, h		≤24
6	Low‑temperature flexibility	Standard condition	No crack or fracture at 0 ℃
7	Elongation at break	Standard condition, %	≥600

Usage Method

Substrate preparation: Remove dust, laitance and oil; clear loose and raised parts. Keep surface flat & solid, damp surface is acceptable without standing water.
Mixing: One‑component: stir thoroughly before use. Two‑component: mix strictly according to ratio until uniform without particles.
Detail reinforcement: Apply 1‑2 coats as extra layer on inside/outside corners, pipe roots and construction joints.
Multi‑coat application: Apply thin coats successively. Next coat can be applied only after previous coat dries. Brush in cross directions to reach designed total thickness.
Curing: Natural curing after finishing. Proceed to next procedure only after full curing.
Protective layer: Apply cement mortar protective layer after film curing for basement and roof projects to prevent mechanical damage.

Cold Applied Bituminous Waterproofing Coating Polymer Modified Asphalt For Engineering Projects

Product Tags:

bituminous waterproofing coating polymer

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Weifang Shihua Chemical Building Material Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!